Influência da espessura e diferentes graus de opacidade do dissilicato de lítio no grau de conversão e resistência de união de cimentos resinosos / Influence of thickness and different degrees of opacity of lithium disilicate on the degree of conversion and bond strength of resin cements

O objetivo desse trabalho foi avaliar a influência de diferentes graus de opacidade e espessuras do dissilicato de lítio no grau de conversão de dois cimentos resinosos e na resistência de união dos mesmos à cerâmica. Duzentos e quarenta amostras cerâmicas de dissilicato de lítio (6x6 mm) foram obtidos a partir de blocos de IPS E-max CAD (Ivoclar Vivadent, Schaan, Liechtensten), nas opacidades HT (alta translucidez), LT (baixa translucidez) e MO (média opacidade), nas espessuras de 0,3 mm, 0,7 mm, 1,2mm, 1,7 mm, 2,0 mm. Para as análises do grau de conversão (n=9) e resistência de união (n=8) foram utilizados um cimento de ativação física (Variolink Esthetic LC) e um cimento dual (Multilink N). Para análise do grau de conversão, as amostras de cimento foram fotoativadas sob as amostras de cerâmica e levadas a um espectrômetro Raman confocal. Para o teste de resistência de união foram confeccionados cilindros de cimento resinoso sobre as amostras cerâmicas e submetidos ao ensaio de microcisalhamento. Os resultados mostraram que o aumento das espessuras causou diminuição no grau de conversão dos dois cimentos em todas as condições estudadas, porém só influenciou negativamente a resistência de união do cimento Variolink Esthetic LC quando unido à cerâmica na opacidade MO. Na comparação entre as opacidades, de maneira geral, a cerâmica de maior translucidez HT apresentou maiores valores de grau de conversão em comparação às outras opacidades. Já para resistência de união, em algumas espessuras as cerâmicas LT e MO apresentaram os maiores valores. O cimento dual Multilink N apresentou os maiores valores nas duas análises comparado ao cimento fotoativado Variolink Esthetic LC. Portanto, o aumento da espessura e da opacidade do material cerâmico podem promover uma diminuição no grau de conversão do cimento. A resistência de união também sofre uma diminuição com o aumento da espessura de cerâmicas mais opacas. No entanto, a maior translucidez do material não garante valores mais altos dessa mesma propriedade(AU)

This research aims to evaluate the influence of different degrees of opacity and thicknesses of lithium disilicate on the degree of conversion of two resin cements and on their bond strength to the ceramic. Two hundred and forty lithium disilicate ceramic samples (6x6 mm) were obtained from IPS E-max CAD (Ivoclar Vivadent, Schaan, Liechtensten), in HT, LT and MO opacities, with thicknesses of 0.3 mm, 0.7 mm, 1.2 mm, 1.7 mm, 2.0 mm. For degree of conversion (n=9) and bond strength analysis (n=8) a light cured (Variolink Esthetic LC) and a dual cured resin cement (Multilink N) were used. To analyze the degree of conversion, the cement samples were light cured under the ceramic samples and taken to a confocal Raman spectrometer. For the bond strength test, resin cement cylinders were made on the ceramic samples that were later subjected to a microshear. The results showed that the increase in thickness caused a decrease on degree of conversion of both cements in all the conditions studied, but it only had an influence on bond strength of Variolink LC cement for MO ceramic. Comparing the opacities, for the degree of conversion, the most translucent ceramics had higher conversion values compared to the less translucent ones in some thicknesses. As for bond strength, in some thicknesses the LT and MO ceramics showed the highest values. The dual cement Multilink showed the highest values of conversion degree and bond strength compared to Variolink Esthetic LC light-cured cement. The Multilink dual cement showed the highest values in both analyzes compared to the Variolink LC light-cured cement. Therefore, increasing the thickness and opacity of the ceramic material can promote a decrease in the degree of cement conversion. The bond strength also suffers a decrease with increasing thickness of more opaque ceramics and the greater translucency of the material does not guarantee higher values of this same property(AU)

Influence of customization and light-curing device on the bond strength of glass fiber posts - in vitro study / Influência da reanatomização e do aparelho fotopolimerizador na resistência de união de pinos de fibra de vidro - estudo in vitro

Introduction: Endodontically treated teeth are usually affected by extensive structure loss requiring the use of intraradicular posts to provide retention and restoration. Objective: An in vitro assessment was performed on the bonding of glass fiber posts to the root dentin. Material and method: Ninety (n = 10) single bovine roots were used in a 3 x 3 x 3 factorial study with subdivided plots: post customization varying the presence and type of resin (without customization, conventional resin, and Bulk Fill resin), light-curing device (Valo, Radii-Cal, Rainbow), and root third (cervical, middle, and apical). Result: For the customization factor, Tukey's test (5%) showed the superiority of the Bulk Fill (8.16 MPa) and Z350 (7.40 MPa) groups compared to the control group (4.92 MPa), without differing from each other. All light-curing devices differed, showing the superiority of Valo (9.36 MPa), Radii (6.96 MPa) as an intermediate, and the inferiority of Rainbow (4.17 MPa). The cervical root third (7.81 MPa) was superior, the apical third was inferior (5.80 MPa), and the middle third (6.88 MPa) was an intermediate without differing from the others. Conclusion: The customization of glass fiber posts increases the bond strength to the root dentin, regardless of the resin used. There was a compromise in the apical third and when using light-curing devices with lower light intensity.

Introdução: Dentes com extensa perda de estrutura podem comprometer a retenção das restaurações ao remanescente dental, onde pinos intraradiculares são indicados. Objetivo: Avaliou-se in vitro a união de pinos de fibra de vidro à dentina radicular em função de diferentes modos de reanatomização, fotopolimerizadores e regionalização radicular. Material e método: Noventa (n=10) raízes bovinas uniradiculares foram usadas num estudo fatorial 3 x 3 x 3 com parcelas subdivididas: Reanatomização do pino, variando a presença e tipo de resina (Sem reanatomização, Resina Convencional e Resina Bulkfill); Fotopolimerizador (Valo, Radii-cal, Rainbow); e Terço radicular (cervical, médio e apical). Resultado: O teste de Tukey (5%) evidenciou para o Fator Reanatomização superioridade dos grupos BulkFill (8.16MPa) e Z350 (7.40MPa) ao grupo Controle (4.92MPa), sem diferirem entre si. Todos os fotopolimerizadores diferiram entre si, com superioridade de Valo (9.36MPa), Radii (6.96MPa) intermediário, e inferioridade de Raiwbow (4.17MPa). O terço radicular cervical (7.81MPa) foi superior e o apical inferior (5.80MPa), com o terço médio (6.88MPa) intermediário e sem diferir dos demais. Conclusão: Conclui-se que a reanatomização de pinos de fibra de vidro aumenta a resistência de união à dentina radicular, independentemente da resina utilizada, havendo prejuízo no terço apical e quando são empregados fotopolimerizadores com menor intensidade luminosa.

Novo sistema de retentor pré-fabricado perfurado e de iluminador em fibra óptica: estudo da resistência mecânica frente a variação dos cimentos resinosos / New system of hollow prefabricated post and optical fiber illuminator: study of the mechanical strength by varying resin cements

O presente estudo teve por objetivo avaliar a resistência à flexão de um pino experimental de fibra de vidro vazado, e a resistência adesiva entre este pino experimental à dentina radicular, associando a utilização de um dispositivo iluminador em fibra óptica, sob o processo de envelhecimento, além de determinar a distribuição de tensão pela Análise de Elementos Finitos (FEA). O pino experimental e o dispositivo iluminador de fibra óptica têm por finalidade aumentar a efetividade de fotoativação dos cimentos resinosos nos terços médios e apicais dos canais radiculares. Para o teste de flexão de 3 pontos, estritamente do pino de fibra de vidro, as amostras foram divididas em 4 grupos (n=10): pino convencional (pc), pino experimental sem preenchimento (pp), com preenchimento de cimento resinoso (ppc) e com preenchimento de fibra óptica (ppf). Para o teste de resistência adesiva Pull-out, 100 raízes de dentes bovinos foram restauradas com retentores intrarradiculares e coroas de resina composta, distribuídos em 10 grupos (n=10), tendo como variáveis: o tipo de pino de fibra de vidro [convencional (C) ou perfurado (P)], o sistema de fotoativação [com ou sem o iluminador de fibra óptica (O)], o tipo de cimento resinoso [fotoativado (F) ou polimerização dual (D)] e o envelhecimento das amostras [com e sem ciclagem mecânica (C)]. O processo de envelhecimento foi realizado através da ciclagem mecânica e as amostras foram submetidas ao teste de resistência adesiva Pull-out. A análise do modo de falha foi realizada em Estereomicroscópio. A Análise em Elementos Finitos avaliou a distribuição de tensão pela análise de von Mises, deformação total e tensão máxima principal no Software Ansys 19.3. A análise estatística foi constituída pelo teste de normalidade Shapiro-Wilk, análise de variância (ANOVA) 1, 2 e 3 fatores e teste Tukey 5%. As médias e desvios padrão de resistência à flexão foram (MPa): pc = 677 ± 81,1; ppc = 419 ± 23,2; ppf = 200 ± 32,5 e pp = 177 ± 32,8. As médias e desvios padrão de resistência adesiva foram (MPa): CD = 12,2 ± 1,21; PD = 11,1 ± 1,32; PF = 10,9 ± 1,29; POD = 13,7 ± 1,16; POF = 11,9 ± 1,48; CDC = 10,1 ± 1,33; PDC = 9,25 ± 1,11; PFC = 8,37 ± 1,25; PODC = 10,8 ± 0,95 e POFC = 9,82 ± 1,02. Os resultados do modo de falha foram: adesiva entre pino e cimento (56%), mista predominantemente adesiva entre cimento e dentina (22%), adesiva entre cimento e dentina (14%) e a mista predominantemente adesiva entre pino e cimento (8%). Concluiu-se que entre os pinos experimentais, o grupo do pino perfurado preenchido com cimento resinoso obteve o maior valor de resistência à flexão, a utilização do dispositivo iluminador aumentou os resultados de resistência adesiva nos grupos dos pinos perfurados e não houve diferença na distribuição de tensões entre os grupos. (AU)

The present study aimed to evaluate the flexural strength of an experimental hollow glass fiber post, and the bond strength between this experimental post and root dentin, associating the use of an optical fiber illuminating device, under the aging process, in addition to determine the stress distribution by Finite Element Analysis (FEA). The experimental post and optical fiber illuminating device are intended to increase the polymerization effectiveness of resin cements in the middle and apical regions of root canals. For the 3-point bending test, strictly of the fiber post, the samples were divided into 4 groups (n=10): conventional post (pc), experimental post without filling (pp), with resin cement filling (ppc) and with optical fiber filling (ppf). For the Pull-out test, 100 roots of bovine teeth were restored with intraradicular retainers and composite resin crowns, distributed into 10 groups (n=10), with the following variables: glass fiber post type [conventional (C) or hollow (P)], the photocuring system [with or without the optical fiber illuminating device (O)], the type of resin cement [light cured (F) or dual cured (D)] and aging of the samples [with and without mechanical cycling (C)]. The aging process was performed by mechanical cycling and the samples were submitted to the Pull-out bond strength test. Failure mode analysis was performed using a stereomicroscope. Finite Element Analysis evaluated the stress distribution by von Mises analysis, total strain and maximum principal stress in Ansys Software 19.3. Statistical analysis consisted of the Shapiro-Wilk normality test, 1-, 2- and 3-way analysis of variance (ANOVA) and Tukey test 5%. The means and standard deviations of flexural strength were (MPa): pc = 677 ± 81.1; ppc = 419 ± 23.2; ppf = 200 ± 32.5 and pp = 177 ± 32.8. The means and standard deviations of bond strength were (MPa): CD = 12.2 ± 1.21; PD = 11.1 ± 1.32; PF = 10.9 ± 1.29; POD = 13.7 ± 1.16; POF = 11.9 ± 1.48; CDC = 10.1 ± 1.33; PDC = 9.25 ± 1.11; PFC = 8.37 ± 1.25; PODC = 10.8 ± 0.95 and POFC = 9.82 ± 1.02. The failure mode results were: adhesive between post and cement (56%), mixed predominantly adhesive between cement and dentin (22%), adhesive between cement and dentin (14%) and mixed predominantly adhesive between post and cement (8 %). It was concluded that among the experimental posts, the hollow post group filled with resin cement obtained the highest flexural strength value, the use of the illuminating device increased the results of bond strength in the hollow post groups and there was no difference in the stress distribution among the groups (AU)

Influência de um novo dispositivo acessório de fotopolimerização com fibra óptica e pino de fibra de vidro experimental nas propriedades mecânicas, físicoquímicas e adesão dos cimentos resinosos / Influence of a new light curing device with optical fiber and an experimental glass fiber post on the physicochemical, mechanical properties and adhesion of resin cement

O objetivo deste estudo foi avaliar in vitro a influência de um novo dispositivo fotopolimerização e pino de fibra de vidro nas propriedades mecânicas, físicoquímicas e adesão dos cimentos resinosos. Foram utilizados oitenta dentes bovinos, submetidos ao tratamento endodôntico, distribuídos em 5 grupos (n=16): CD (Pino fibra vidro e cimento dual); PF (Pino perfurado e cimento fotoativado); PD (Pino perfurado e cimento dual); POF (Pino perfurado iluminador de fibra óptica e cimento fotoativado); POD (Pino perfurado iluminador de fibra óptica e cimento dual). Os dentes foram preparados para colocação de um protótipo de pino em fibra de vidro que possui um canal interno de diâmetro regular e com conicidade progressiva. A perfuração permite a inserção da fibra óptica ao longo da extensão do pino a fim de possibilitar a ação da luz ao longo de todo o comprimento do conduto radicular. Após a cimentação, os espécimes foram seccionados perpendicularmente, e obtida 1 fatia de 2 mm de espessura do terço apical, médio e cervical. A avaliação mecânica foi realizada através do ensaio de push-out para determinação da resistência adesiva nos terços cervical, médio e apical seguido pela análise da fratura em estereomicroscópio. Os retentores intrarradiculares foram também submetidos ao teste de flexão de 3 pontos para análise do material preenchedor do pino de fibra (n=10). As análises físico - químicas foram realizadas através da determinação do grau de conversão dos cimentos (RAMAN) e análise em espectroscopia de energia dispersiva (EDS) dos monômeros presentes. A adesão foi analisada pela interface de cimentação pelo MEV e reconstrução 3D do novo sistema através do Micro-CT. Os dados obtidos foram analisados estatisticamente pelo ANOVA (um e dois fatores) e comparação múltipla de Tukey, (p<0,05). Os resultados de resistência adesiva evidenciaram que o terço apical obteve o maior valor de resistência adesiva em comparação ao terço médio (p<0,001), o grupo POD do terço apical foi estatisticamente significante em relação ao grupo CD do terço médio (p<0,001). Na analise individual de cada terço, não houve diferença entre os grupos experimentais e o controle (p>0,05). A falha adesiva entre cimento e dentina foi a mais predominante entre todos os grupos e terços. O pino de fibra de vidro (controle) obteve o maior valor de resistência à flexão (p<0,001), seguido do pino de fibra de vidro perfurado preenchido com cimento resinoso (p<0,001). Os maiores valores de GC foram alcançados pelo grupo POD com 82,3% (cervical) 69,9 % (médio) e 76,21% (apical) e o EDS comprovou a presença de componentes químicos adequados. A análise da adesão do novo pino de fibra de vidro comprova uma excelente adaptação no interior do canal radicular nas regiões cervical, médio e apical. Portanto o novo dispositivo com fibra óptica e pino de fibra de vidro experimental aumentaram as propriedades mecânicas, físico-químicas e adesão do cimento resinoso (AU)

The aim of this study was to evaluate in vitro the influence of a new light curing device with optical fiber and experimental glass fiber post on the physicochemical, mechanical, and adhesion properties of resin cements. Eighty bovine teeth were used, submitted to an endodontic treatment, distributed in 5 groups (n=16): CD (Glass fiber post and dual cement); PF (Perforated post and light-cured cement); PD (Perforated post and dual cement); POF (Fiber optic illuminating with a perforated post and lightcured cement); POD (Fiber optic illuminating with a perforated post and dual cement). The teeth were prepared for placement of a glass fiber post prototype, which has an internal canal of regular diameter and progressive taper. The internal perforation extension allows the insertion of the optical fiber along the entire length of the post in order to allow the action of light along the entire length of the root canal.The specimens were sectioned perpendicularly for the tests, and 1 slice approximately 2 mm thick was obtained from the apical, middle and cervical thirds. The mechanical evaluation was carried out through the push-out test to determine the adhesive bond strength, in the cervical, middle and apical thirds, followed by the fracture analysis under a stereomicroscope, the intraradicular post were also submitted to the 3-point bending test for material analys of the fiber post filler (n=10). The physicochemical analyzes were performed by determining the degree of conversion of the cements (RAMAN) of each sample and the analysis of energy dispersive spectroscopy (EDS) of the monomers present. Adhesion was analyzed by the cementation interface and 3D reconstruction of the new system through micro-CT, and finally, SEM analysis of the adhesive interface. The data obtained were analyzed for normality and statistically by ANOVA (one and two ways) and Tukey's multiple comparison (p<0.05). The adhesive bond strength results showed that the apical third had the highest value of adhesive strength compared to the middle third (p<0.001), and the POD group of the apical third was statistically significant in relation to the CD group of the middle third (p<0.001). In the individual analysis of each third, there was no difference between the experimental and control groups (p>0.05). Adhesive failure between cement and dentin was the most prevalent among all groups and thirds. The conventional post (control) had the highest flexural strength value (p<0.001), followed by the perforated fiberglass post filled with resin cement (p<0.001). The POD group achieved the highest GC values with 82.3% (cervical), 69.9% (medium), and 76.21% (apical) and EDS confirmed the presence of adequate chemical components. The analysis of the adhesion of the new fiberglass post proves an excellent adaptation inside the root canal in the cervical, middle and apical regions. Therefore, the new light curing device with optical fiber and experimental glass fiber post improved the resin cement's mechanical, phycochemical, and adhesion. (AU)

Use of Self-Adhesive Resin Cements in Dentistry: a Literature Review / Uso de Cimentos Resinosos Autoadesivos em Odontologia: uma Revisão da Literatura

Self-adhesive resin cements (SARCs) are cementing agents and have the objective of simplifying adhesive cementation, with a simplified use protocol. The aim of this article was to review the literature on SARCs with a focus on the advantages of their use, highlighting their adhesion and biocompatibility mechanism. Thus, the Health Sciences Descriptors "Self-Adhesive Resin Cement", "Dental Cements", "Adhesion" and "Dental Prosthesis" were used, as well as their Portuguese counterparts in the online databases SciELO, PubMed and Bireme in the period of time between the years 2000 to 2020. According to the studies, SARCs have excellent physical and mechanical properties, which include low solubility in the oral environment, adhesion to the dental substrate and the prosthetic part, color mimicry, biocompatibility and fluoride release, in addition to being applied in a single step, optimizing the operator's working time. In addition, self-adhesive cements seem to offer a promising new approach in indirect restorative procedures, which may present a performance similar to conventional ones, however more studies are needed to support their long-term applicability. (AU)

Os cimentos resinosos autoadesivos (CRAAs) são agentes de cimentação e possuem o objetivo de simplificar a cimentação adesiva, com um protocolo simplificado de utilização. Assim, o objetivo deste trabalho foi revisar na literatura acerca dos CRAAs com enfoque nas vantagens de sua adequada utilização, evidenciando seu mecanismo de adesão e biocompatibilidade. Dessa forma, foram utilizados os descritores em Ciências da Saúde (DeCS) "Cimento Resinoso Autoadesivo", "Cimentos Dentários", "Adesão" e "Prótese Dentária", assim como seus correspondentes na língua inglesa nas bases de dados online SciELO, PubMed e Bireme no período de tempo entre os anos 2000 a 2020. De acordo com os estudos, os CRAAs apresentam excelentes propriedades físicas e mecânicas, que incluem baixa solubilidade no meio bucal, adesão ao substrato dental e a peça protética, mimetização de cores, biocompatibilidade e liberação de fluoretos, além de serem aplicados em uma única etapa clínica, otimizando o tempo de trabalho do operador. Além disso, os cimentos autoadesivos oferecem uma nova abordagem promissora em procedimentos restauradores indiretos, podendo apresentar um desempenho semelhante aos convencionais, porém são necessários mais estudos que sustentem sua aplicabilidade a longo prazo. (AU)

One Year Clinical Evaluation of White Spot Lesions with Newly Introduced Resin Modified Glass-Ionomer in Comparison to Resin Infiltration in Anterior Teeth: a split mouth randomized controlled clinical trial from Egypt / Avaliação clínica de um ano de lesões de mancha branca com iônomo de vidro modificado por resina recentemente introduzido em comparação à infiltração de resina em dentes anteriores: um ensaio clínico controlado randomizado de boca dividida do Egito

Objective: to compare the clinical performance of newly introduced resin modified glass ionomer varnish (Clinpro™ XT) versus resin infiltration in treatment of post-orthodontic white spot lesions. Material and Methods: Six participants (70 teeth) were enrolled with post-orthodontic white spot lesions. Randomization was performed according to patient selection for the sealed envelope containing which half will receive the control (resin infiltration (ICON, DMG) and the other will receive the intervention (resin modified glass-ionomer cement varnish (Clinpro™ XT, 3M)). Follow up was done after 1 day, 1 week, 1 month, and 3 months, 6 months and 12 months. The color was assessed by spectrophotometer while the degree of demineralization was measured by Diagnodent pen 2910. Patient satisfaction was assessed using (VAS) Visual analogue scale Results:Regarding color change, significant improvement in lightness for ICON group, while Clinpro™ XT group, the change was insignificant. The demineralization data revealed significant decrease in demineralization with resin infiltration after immediate application. Clinpro™ XT showed also significant decrease after immediate assessment and significant increase in demineralization in 6 and 12 months. Conclusion: Resin infiltration can be considered more as an alternative treatment rather than fluoride varnish. Clinpro™ XTis considered as a preventive protocol, provided that renewal application is needed after 3 months (AU)

Objetivo: comparar o desempenho clínico do recém-introduzido verniz de ionômero de vidro modificado por resina (Clinpro ™ XT) com a infiltração de resina no tratamento de lesões de manchas brancas pós-ortodônticas. Material e Métodos: Seis participantes (70 dentes) foram inscritos com lesões pós-ortodônticas de manchas brancas. A randomização foi realizada de acordo com a seleção do paciente para o envelope lacrado contendo qual metade receberá o controle (infiltração de resina (ICON, DMG) e a outra metade receberá a intervenção (verniz de cimento de ionômero de vidro modificado por resina (Clinpro ™ XT, 3M)). O acompanhamento foi feito após 1 dia, 1 semana, 1 mês e 3 meses, 6 meses e 12 meses. A cor foi avaliada por espectrofotômetro, enquanto o grau de desmineralização foi medido pela caneta Diagnodent 2910. A satisfação do paciente foi avaliada usando (VAS) Escala visual analógica. Resultados: Em relação à mudança de cor, houve uma melhora significativa na luminosidade para o grupo ICON, enquanto o grupo Clinpro ™ XT, a mudança foi insignificante. Os dados de desmineralização revelaram diminuição significativa da desmineralização com infiltração de resina após a aplicação imediata. O grupo Clinpro ™ XT também mostrou diminuição significativa após avaliação imediata e aumento significativo na desmineralização em 6 e 12 meses. Conclusão: A infiltração de resina pode ser considerada mais como uma alternativa de tratamento do que o verniz fluoretado. O Clinpro ™ XT é considerado um protocolo preventivo, uma vez que a renovação é necessária após 3 meses. (AU)

Effect of antioxidant agents after dental bleaching on luting of ceramic laminates / Efeito de agentes antioxidantes pós-clareamento na cimentação de laminados cerâmicos

O objetivo deste estudo in vitro foi avaliar o efeito da aplicação de agentes antioxidantes após o clareamento dentário e previamente à cimentação de laminados cerâmicos na estabilidade cromática do conjunto restaurador, assim como nas propriedades mecânicas de nanodureza (HIT), módulo de elasticidade (Eit*), grau de conversão, resistência de união e morfologia da interface adesiva. Ademais, a neutralização de peróxido de hidrogênio e a caracterização superficial do esmalte, como ângulo de contato, energia de superfície, energia livre total de interação, microscopia eletrônica de varredura e espectroscopia de energia dispersiva do substrato submetido à ação das soluções antioxidantes e do agente clareador também foram analisados. Duzentos e quarenta e dois blocos de esmalte dentário (7x8x0,6mm) foram utilizados para o processo de cimentação e distribuídos em grupos experimentais de acordo com os métodos de procedimentos (grupo não clareado, grupo clareado com Whiteness HP Maxx 35%), tipos de antioxidantes adotados (controle; ácido ascórbico 10% e α-tocoferol 10%) e períodos de cimentação (após 24 horas e 14 dias do processo de cimentação) (n = 22). Foi utilizado o sistema adesivo Tetric N Bond Universal e o cimento resinoso Variolink Esthetic LC (Ivoclar Vivadent) como agentes cimentantes. Os dados foram submetidos a testes estatísticos de normalidade e analisados por ANOVA e teste de Tukey (α = 0,05). Os dados da morfologia da interface adesiva, obtidas pela microscopia confocal a laser, foram submetidas ao teste Kappa inter-examinadores e os dados foram submetidos aos testes Kruskal-Wallis e Dunn (α = 0,05). Os resultados mostraram que, de modo geral, a utilização da solução antioxidante α-tocoferol 10% pós-clareamento no período mediato promoveu resultados satisfatórios com relação à estabilidade cromática do conjunto restaurador, assim como para as propriedades mecânicas, grau de conversão, resistência de união e morfologia da interface adesiva comparado ao grupo clareado sem associação dos agentes antioxidantes, tanto para o período mediato, quanto para o período de 14 dias (p< 0,05). A solução de αtocoferol 10% apresentou maiores valores de neutralização do peróxido de hidrogênio e maiores valores de molhabilidade do esmalte em relação aos grupos controle e ácido ascórbico (p< 0,05). A energia de superfície e energia livre total de interação do esmalte dentário foi significativamente influenciada pelo tratamento clareador (p< 0,05). Dessa forma, conclui-se que o emprego da solução antioxidante α-tocoferol 10% promoveu resultados promissores, sugerindo que o mesmo poderia ser utilizado mediatamente após o clareamento dental na cimentação de laminados cerâmicos(AU)

The aim of this in vitro study was to evaluate the effect of antioxidant agents application after tooth bleaching and prior to luting of ceramic veneers on color stability of the restorative set, as well as on mechanical properties of nanohardness (HIT), elastic modulus (Eit*), degree of conversion, bond strength and morphology of the adhesive interface. Furthermore, the hydrogen peroxide neutralization and surface characterization of enamel, such as contact angle, surface energy, total free energy of interaction, scanning electron microscopy and energy-dispersive spectroscopy of the substrate submitted to the action of antioxidant solutions and bleaching agent were also analyzed. Two hundred forty two dental enamel blocks (7 x 8 x 0.6 mm) were used for the luting process and distributed into experimental groups according to the procedure methods (unbleached group, bleached group with Whiteness HP Maxx 35%), types of antioxidants adopted (control; 10% ascorbic acid and 10% α-tocopherol) and the luting periods (24 hours and 14 days after the luting process) (n = 22). Tetric N Bond Universal adhesive system and Variolink Esthetic LC resin cement (Ivoclar Vivadent) were used as luting agents. Data were submitted to statistical tests of normality and analyzed by ANOVA and Tukey tests (α = 0.05). The adhesive interface morphology data, obtained by confocal laser microscopy, were submitted to the interexaminer Kappa test and the data were submitted to Kruskal-Wallis and Dunn´s tests (α = 0.05). The results showed that, in general, the use of 10% α-tocopherol antioxidant solution after bleaching in mediate period promoted satisfactory results regarding the color stability of the restorative set, as well as for the mechanical properties, degree of conversion, shear bond strength and adhesive interface morphology compared to the bleached group without antioxidant agents association, both for the mediate and 14-day period (P < 0.05). The 10% αtocopherol solution showed higher hydrogen peroxide neutralization values and higher enamel wettability values compared to the control and ascorbic acid groups (P < 0.05). Surface energy and total free energy of interaction of tooth enamel were significantly influenced by the bleaching treatment (P < 0.05). Thus, it is concluded that the use of 10% αtocopherol antioxidant solution promoted promising results, suggesting that it could be used mediately after tooth bleaching on luting of ceramic laminates(AU)

Retention of cemented zirconia copings on TiBase abutments / Retenção de copings de zirconia cimentados sobre pilares tibase

ABSTRACT This study evaluated the influence of resin cements and glass ionomers on tensile strength and types of failure of zirconia copings cemented on titanium base abutments. Forty-two samples were prepared, which were formed by a Cone Morse implant, a titanium abutment with the fixing screw, and a zirconia structure made using a CAD/CAM system. The samples (n = 42) were randomly distributed according to the cementing agent: resin-modified glass ionomer cement (RelyX Luting 2), self-adhesive resin cement (RelyX U200), and self-curing resin cement (Multilink N). After cementation of the copings, half of the samples from each group (n = 7) were randomly selected and subjected to thermocycling (5000 cycles). A tensile load test was performed on a universal testing machine until failure occurred (1 mm). In addition, the type of failure was analyzed using the two-way analysis of variance test and Tukey's post-hoc test (α = 0.05). Lower tensile load was observed for the glass ionomer cement (p < 0.001) regardless of the evaluation period. After thermocycling, a significant reduction in tensile load values was verified for both evaluated cements (p = 0.047). For the resin cements, failures were predominantly of the screw fracture type (82.1%) already with the use of glass ionomer cement, and 28.5% of the failures were of an adhesive type between the zirconia coping and the cement. Resin cements have better stability under tensile load compared to resin glass ionomers when cementing zirconia copings on titanium base abutments.

RESUMO Este estudo avaliou influência dos cimentos resinosos e a base de ionômero de vidro na resistência à tração e os tipos de falhas de copings de zircônia cimentados sobre pilares TiBase. Foram confeccionadas 42 amostras, sendo estas formadas por implante cone morse, pilar de titânio (TiBase) com o parafuso de fixação e uma estrutura de zircônia (coping de Zr) confeccionado através do sistema CAD/CAM. As amostras (n =42) foram aleatoriamente distribuídas de acordo com o agente de cimentação: (cimento de ionômero de vidro modificado por resina [RelyXTMLuting2]; cimento resinoso autoadesivo [RelyXTM U200] e cimento resinoso autopolimerizavel (Multilink® N). Após cimentação dos copings, metade das amostras de cada grupo (n = 7) foram aleatoriamente selecionadas e submetidas a termociclagem (5000 ciclos). O Teste de resistência a tração foi realizado em uma máquina de ensaio universal, até que ocorresse a falha (1 mm/min). Adicionalmente, o tipo de falha foi analizado. Os dados foram analisados pelo teste ANOVA two-way e post teste de Tukey's (α = 0.05). Menor média de resistência a tração foi observada para o cimento de ionômero de vidro (p < 0,001) independente do período de avaliação. Após a termociclagem, foi verificada uma redução significativa nos valores de resistênca a tração, para os cimentos avaliados (p=0,047). Para os cimentos resinosos, as falhas foram predominantemente do tipo fratura do parafuso (82,1%) já com o uso do cimento de ionômero de vidro, 28,5% das falhas foram de tipo adesiva entre o coping de Zr e o cimento. Cimentos resinosos apresentam melhor estabilidade na resistência a tração em comparação a ionmeros de vidro resinosos na cimentação de copings de zircônia sobre pilares TiBase.

Influência do material cerâmico, cimento e tipo de substrato na qualidade estética de restaurações indiretas / Influence of ceramic material, resin cement and type of substrate in the aesthetic quality of indirect restorations

O objetivo deste estudo foi avaliar a influência do material cerâmico, cimento e tipo de substrato na qualidade estética de restaurações indiretas. A pesquisa científica foi dividida em duas partes. Na primeira análise, a alteração de cor e luminosidade de restaurações cerâmicas à base de dissilicato de lítio (e.max CAD), monossilicato de lítio (Celtra Duo) e cerâmica híbrida (Vita-Enamic CAD) foram analisadas quando sobrepostas em diferentes substratos (esmalte bovino, metal e zircônia), após a aplicação de pastas de prova "try-in" e após a cimentação com diferentes tipos de cimentos resinosos (RelyX Veneer, Variolink Esthetic LC e RelyX Ultimate). As análises foram realizadas em espectrofotômetro de reflexão UVVisivel (n=6). Os resultados mostraram que o tipo de substrato influenciou de maneira mais significante a estabilidade de cor e luminosidade das cerâmicas, independente da cor e tipo de material de cimentação. No segundo projeto, o objetivo foi avaliar a alteração cromática e a transmitância de diferentes restauraçoes cerâmicas: dissilicato de lítio (e.max CAD), monossilicato de lítio (Celtra Duo) e cerâmica híbrida (Vita-Enamic CAD) em oito diferentes espessuras (0,3mm à 2,0mm), com variação da potência do fotopolimerizador (1000mW/cm2 e 3200mW/cm2 ) e submetidos ao envelhecimento UV. As análises da alteração cromática foram realizadas em espectrofotômetro de reflexão UV-Visivel (n=8), enquanto que a análise da transmitância das cerâmicas foi realizada medindo-se a radiação de luz transmitida pelos diferentes materiais com um medidor de potência. Os resultados obtidos mostraram que os materiais cerâmicos estudados apresentam comportamentos diferentes quanto a estabilidade de cor das peças cimentadas. As diferentes espessuras influenciaram na cor do conjunto após o envelhecimento UV em todos os materiais estudados, sendo que a cerâmica de dissilicato de lítio e a cerâmica híbrida apresentaram influência nas espessuras mais delgadas. A transmitância dos materiais foi influenciada pela sua espessura e composição. A variação da potência do fotopolimerizador não influenciou na estabilidade de cor de todos os materiais analisados nas diferentes espessuras(AU)

The aim of this study was to evaluate the influence of ceramic material, resin cement and type of substrate in the aesthetic quality of indirect restorations. The research was divided into two chapters. In the first analysis, the color difference and luminosity of lithium disilicate (e.max CAD), zirconia-reinforced lithium silicate (Celtra Duo) and polymer infiltrated ceramic network (Vita Enamic CAD) were analyzed on different substrates (bovine enamel, metal and zirconia), after try-in pastes placed between the ceramics and substrates and after luting with different resin cements (RelyX Veneer, Variolink Esthetic LC e RelyX Ultimate) (n=6). The results showed that the type of substrate had more influence on the color stability and luminosity of ceramics, independent of the color and resin cement used. In the second study, the aim was to evaluate the color difference and transmittance of different ceramic restorations: lithium disilicate (e.max CAD), zirconia-reinforced lithium silicate (Celtra Duo) and polymer infiltrated ceramic network (Vita Enamic CAD) in eight thickness (0.3mm to 2.0mm), using light-emitting diode Valo Cordless (Standard and Xtra power modes) submitted to UV aging (n=8). The transmittance was done measuring the light transmitted through the materials with a power meter. The results showed that the ceramic materials showed different behavior in the color stability, especially for the thinner lithium disilicate and polymer infiltrated ceramic network materials. The transmittance was influenced by the thickness and composition of the materials. The variation in the power intensity of the lightemitting diode did not influence the color stability of the materials, independent of its thickness(AU)

Influence of Different Surface Treatments on the Bond Strength Between Composites and Resin Cement / INFLUÊNCIA DE DIFERENTES TRATAMENTOS DE SUPERFÍCIE NA RESISTÊNCIA DE UNIÃO ENTRE COMPÓSITOS E CIMENTO RESINOSO

The aim of this study was to evaluate the influence of different surface treatments on bond strength (BS) between composite and a resin cement trough microshear bond strength test. Seventy five discs (10x2 mm) of Filtek P90, Filtek Z250 and Filtek Z350 XT (3M ESPE), were divided into 5 groups according to the treatment: C= control - no treatment; sandblasting J= aluminum oxide (50µm); sandblasting JE = + 99.3% ethanol for 5 min; silica coating S = (3M-ESPE Cojet - 30 microns); SS = silica coating + silane. PVC tubes (0.5 x 0.80 mm) were attached on the composite disc, and then, inserted resin cement (3M ESPE-RelyX ARC). After 24 hours artificial saliva storage at 37oC, the specimens were tested for microshear crosshead speed of 1.0 mm/min. Data were evaluated in two-way ANOVA and Tukey's test (5%) for contrast. The results showed that sandblasting with aluminum oxide (J) was efficient in increasing the BS for composites Z350 and P90. For the Z250, there were no difference between treatments. Also, CS showed results similar to controls for all composites. SE showed the worst results for Z350 e P90. BS values were dependent on the type of composite and the surface treatment used. Sandblasting with aluminum oxide seems to be an effective surface treatment for composites and may lead to higher BS values, while the use of ethanol could be harmful.

O objetivo deste estudo foi avaliar a influência de tratamentos de superfície na resistência de união (RU) entre compósitos e um cimento resinoso. Setenta e cinco discos (10x2 mm) das resinas Filtek P90, Filtek Z250 e Filtek Z350 (3M ESPE) foram divididos em 5 grupos de acordo com o tratamento: N= sem tratamento; S= jateamento com óxido de alumínio (50µm); SE= jateamento de óxido de alumínio + 99,3% de etanol por 5 min; C= jateamento de sílica com Cojet - 30 microns (3M ESPE); CS= jateamento de sílica + silano. Tubos de PVC (0,5 x 0,80 mm) foram fixados nos discos e o cimento resinoso (RelyX ARC, 3M ESPE) foi inserido. Após 24 horas de armazenamento em saliva artificial a 37oC, os espécimes foram submetidos ao teste de microcisalhamento com velocidade de 1,0 mm/min. Os dados foram avaliados em ANOVA de dois fatores e no teste de Tukey (5%) para contraste. Os resultados mostraram que o tratamento com oxido de alumínio (J) foi eficiente no aumento da RU nos compósitos Filtek Z350 e P90. Não houve diferença entre tratamentos para a Z250. Grupo CS mostrou resultados semelhantes aos do controle para todos os compósitos. Já o SE mostrou os piores resultados de RU. Concluiu-se que os valores de RU foram dependentes do tipo de compósito e do tratamento de superfície utilizado. O jateamento com óxido de alumínio parece ser um tratamento de superfície eficaz e pode elevar os valores de RU, já o uso de etanol pode ser prejudicial

Effect of two processing techniques used to manufacture lithium disilicate ceramics on the degree of conversion and microshear bond strength of resin cement / Efeito de duas técnicas de processamento utilizadas na fabricação da cerâmica de dissilicato de lítio no grau de conversão e na resistência de união ao microcisalhamento do cimento resinoso

ABSTRACT The aim of the current study was to compare the effect of two lithium disilicate ceramic processing techniques (pressing and CAD/CAM) on the degree of conversion of resin cement when it is photoactivated and the microshear bond strength of resin cement to ceramics. Two ceramic discs were manufactured: one by the Press technique and another by CAD/CAM technique. Five Variolink Veneer resin cement samples were photoactivated through each ceramic disc and subjected to attenuated total reflectance Fourier transform infrared spectroscopy to evaluate their degree of conversion. To evaluate microshear bond strength, 20 ceramic bars were prepared: 10 using the Press technique and 10 using the CAD/CAM technique. The bars were air abraded with 50-μm Al2O3 particles, treated with 10% hydrofluoric acid for 20 s and subjected to RelyX Ceramic Primer application. Adper Scotchbond Multi-Purpose Adhesive was applied to the bars and cured for 10 s. Two 1-mm-height plastic tubes were placed on each bar and filled with Variolink Veneer resin cement. Each cylinder was cured for 20 s. Then the plastic tubes were removed and the microshear bond strength of each cylinder was tested. Data for degree of conversion (%) and microshear bond strength (MPa) were subjected to Student's t-test (α = 0.05). Both degree of conversion of resin cement photoactivated through ceramic and microshear bond strength of resin cement to ceramic were statistically higher in the group in which ceramic was prepared by CAD/CAM technique (44.74% and 22.18 MPa) than in the group in which the ceramic was prepared by the Press technique (25.71% and 19.83 MPa). The lithium disilicate ceramic processing techniques affected the degree of conversion of resin cement when it is photoactivated through the ceramics and the microshear bond strength of resin cement to ceramics.

RESUMO O objetivo do presente estudo foi comparar o efeito de duas técnicas de processamento da cerâmica de dissilicato de lítio (prensada e CAD/CAM) no grau de conversão do cimento resinoso quando fotoativado e na resistência de união ao microcisalhamento do cimento resinoso às cerâmicas. Foram fabricados dois discos de cerâmica: um pela técnica prensada e outro pela técnica CAD/CAM. Cinco amostras de cimento resinoso Variolink Veneer foram fotoativadas através de cada disco cerâmico e submetidas à espectroscopia no infravermelho por transformada de Fourier com reflectância total para avaliar seu grau de conversão. Para avaliar a resistência de união ao microcisalhamento, foram preparadas 20 barras de cerâmicas: 10 utilizando a técnica prensada e 10 utilizando a técnica CAD/CAM. As barras foram tratadas com partículas de Al2O3 (50 μm), com ácido fluorídrico a 10% por 20 s e submetidas à aplicação do RelyX Ceramic Primer. Em seguida, o adesivo multiuso Adper Scotchbond foi aplicado nas barras e fotoativado por 10 s. Dois tubos de plástico de 1 mm de comprimento foram colocados em cada barra e preenchidos com cimento resinoso Variolink Veneer. Cada cilindro foi fotoativado por 20 s. Os tubos de plástico foram removidos e a resistência de união ao microcisalhamento de cada cilindro foi testada. Os dados de grau de conversão (%) e resistência de união ao microcisalhamento (MPa) foram submetidos ao teste t de Student (α = 0,05). Tanto o grau de conversão do cimento resinoso fotoativado através da cerâmica quanto a resistência de união do cimento resinoso à cerâmica foram estatisticamente maiores no grupo em que a cerâmica foi confeccionada pela técnica CAD/CAM (44,74% e 22,18 MPa) do que no grupo em que a cerâmica foi confeccionada pela técnica prensada (25,71% e 19,83 MPa). As técnicas de processamento de cerâmica dissilicada de lítio afetaram o grau de conversão do cimento resinoso quando fotoativado através das cerâmicas e a resistência de união do microcisalhamento do cimento resinoso às cerâmicas.

Influência do Condicionamento Ácido na Resistência de União entre Cerâmica Feldspática e Cimento Resinoso / Influence of Acid Etching on Bond Strength Between Feldspathic Ceramics and Resin Cement

Objetivo: Analisar a influência da resistência de união entre cimento resinoso e cerâmica feldspática utilizando concentrações e tempos de aplicação diferentes de acído fluorídrico (HF). Material e Métodos: Foram confeccionados 18 discos de cerâmica feldspática (Ø10mm - 2mm de espessura) através da técnica incremental, que foram incluídos em resina acrílica e regularizados com lixas de carbeto de silício com granulações de 600, 1200 e 2000 através de uma máquina de polimento com velocidade de 600 rpm para regularização. Logo após foram mergulhadas em água destilada durante 10 minutos em cuba ultrassônica. Todos corpos de prova foram condicionados com HF e silanizados. Foram confeccionados quatro cilindros de cimento sobre cada corpo de prova (n=12), feitos com cimento resinoso Relyx ARC. Logo após, dividiu-se em seis grupos de acordo com o protocolo de tratamento de superfície: G1 (5% - 40s); G2 (5% - 60s); G3 (5% - 80s); G4 (10% - 40s); G5 (10% - 60s) e G6 (10% - 80s). Os corpos de prova foram submetidos ao Teste de Microcisalhamento, com força vertical a uma velocidade de 0,5 mm/min sobre a peça. A resistência de união ao microcisalhamento foi calculada e expressa em Megapascal (MPa). Os dados foram submetidos à análise de variância (ANOVA) dois fatores e para comparações múltiplas foi utilizado o Teste de Tukey, sendo o nível de significância de 5%. Resultados: Quando analisado a concentração do HF, não houve diferenças estatísticas (p>0,05). Na comparação dos tempos de aplicação, G3 (5% - 80s) e G6 (10% - 80s) obtiveram maiores resultados de resistência ao microcisalhamento que os demais grupos. Conclusão: As diferentes concentrações de HF não influenciaram na resistência de união entre cerâmica feldspática e cimento resinoso. Já o aumento do tempo de condicionamento com HF afetou na resistência de união

Objective: analyze the influence of bond strength between resin cement and feldspathic ceramics using different concentrations and application times of hydrofluoric acid (HF). Materials and Methods: 18 feldspathic ceramic discs (Ø10mm - 2mm thickness) were made through the incremental technique, which were included in acrylic resin and regularized with silicon carbide sandpaper with granulations of 600, 1200 and 2000 through a polishing machine with a speed of 600 rpm. Soon after, they were immersed in distilled water for 10 minutes in an ultrasonic bath. All specimens were conditioned with HF and silanized. Four cement cylinders were made on each specimen (n=12), manufactured with Relyx ARC resin cement. After that, it was divided into six groups according to the surface treatment protocol: G1 (5% - 40s); G2 (5% - 60s); G3 (5% - 80s); G4 (10% - 40s); G5 (10% - 60s) e G6 (10% - 80s). The specimens were subjected to the Microshear Test, with vertical force at a speed of 0.5 mm min on the specimen. The microshear bond strength was calculated and expressed in Megapascal (MPa). The data were submitted to two-way analysis of variance (ANOVA) and Tukey's test for multiple comparisons, with a significance level of 5%. Results: when the concentration of HF was analyzed, there were no statistical differences (p>0.05). In the comparison of application times, G3 (5% - 80s) and G6 (10% - 80s) obtained higher results of microshear resistance than the other groups. Conclusion: The different concentrations of HF did not influence the bond strength between feldspathic ceramics and resin cement. However, the increase in the time of HF conditioning affected in the bond strength.

Efeito de tratamentos de superfície da resina, cimento resinoso e envelhecimento nas características interfaciais de restaurações semidiretas de resina composta / Effect of resin surface treatments, resin cement and aging on the interfacial characteristics of semi-direct composite resin restorations

A técnica semidireta realizada com resina composta pode ser uma excelente opção de tratamento para restaurações profundas e extensas em dentes posteriores devido às dificuldades técnicas no uso da resina composta pela técnica direta, como também pelos maiores custo e tempo de tratamento das restaurações indiretas com porcelana. O objetivo do estudo foi avaliar o efeito de diferentes tratamentos da superfície da restauração, tipos de cimento resinoso para cimentação e tempos de envelhecimento na durabilidade de união à dentina, padrão de falhas e nanoinfiltração de restaurações semidiretas. Foram utilizados 320 incisivos bovinos (N=320), dos quais foram obtidos discos de 4.0 mm de espessura e, na sua porção mais central, foi confeccionado um preparo cavitário cônico com 4.8 mm de diâmetro superior e 2.8 mm de diâmetro inferior. As amostras foram divididas em 16 grupos de acordo com o cimento resinoso: RelyX Ultimate (ULT) e RelyX U200 (U200); tratamento de superfície da resina: Silano (S), Single Bond Universal (SBU) e S+SBU; e tempo de envelhecimento: 24 horas (24h) e 6 meses (6m). As análises realizadas foram: Resistência de União à extrusão por push out (RU), Padrão de Falha (PF) e Nanoinfiltração (NI). Os dados foram analisados através de estatística descritiva e inferencial utilizando ANOVA Three Way com Post Hoc de Tukey (p<0,005). Para RU, ULT apresentou melhor desempenho em ambos os tempos de envelhecimento. SBU apresentou melhores resultados após 6 m quando associado ao ULT. As médias aumentaram com o tempo para o U200, exceto quando o silano foi utilizado como tratamento de superfície. Na análise do PF, o ULT apresentou o maior percentual de falha mista, quando a fratura ocorreu simultaneamente em dentina ou material restaurador e na interface adesiva, em ambos os tempos de envelhecimento e quando foi utilizado associado ao SBU ou ao S+SBU como tratamento de superfície da resina. Os diferentes tratamentos de superfície e tempos de envelhecimento não influenciaram a nanoinfiltração na interface cimento-resina. De acordo com os resultados encontrados nesse estudo laboratorial, observou-se um melhor desempenho para o ULT e entre os tratamentos de superfície, o uso de SBU possibilitou maior RU após 6 meses quando utilizado com esse cimento, porém não influenciou a nanoinfiltração na interface cimento-resina. Sugere-se que as restaurações semidiretas de resina composta podem ser cimentadas com ULT com SBU como tratamento de superfície da resina, como também com U200, sem a necessidade de nenhum tratamento químico na restauração (AU).

The semi-direct technique performed with composite resin can be an excellent treatment option for deep and extensive restorations on posterior teeth due to technical difficulties in the use of composite resin by the direct technique, as well as the higher cost and time of treatment of indirect restorations with porcelain. The aim of the study was to evaluate the effect of different treatments of the restoration surface, types of resin cement for cementation and aging times on the bond durability to dentin, failure pattern and nanoleakage of semi-direct restorations. 320 bovine incisors were used (N = 320), from which discs of 4.0 mm thickness were obtained and, in its most central portion, a conical cavity preparation with 4.8 mm in diameter and 2.8 mm in diameter was made. The samples were divided into 16 groups according to the resin cement: RelyX Ultimate (ULT) e RelyX U200 (U200); resin surface treatment: Silane (S), Single Bond Universal (SBU) and S+SBU; and aging time: 24 hours (24h) and 6 months (6m). The analyzes performed were: Bond Strength to push-out extrusion (BS), Failure Pattern (FP) and Nanoleakage (NL). The data were analyzed using descriptive and inferential statistics using ANOVA Three Way with Tukey's Post Hoc (p <0.005). For BS, ULT showed better performance in both times of aging. SBU showed better results after 6m when associated with ULT. The averages increased with time for U200, except when silane was used as a surface treatment. In the analysis of the FP, the ULT presented the highest percentage of mixed failure, when the fracture occurred simultaneously in dentin or restored material and at the adhesive interface, at both times of aging and when it was used in association with SBU or S + SBU as treatment resin surface. The different surface treatments and aging times did not influence nanoleakage at the cement-resin interface. According to the results found in this laboratory study, a better performance was observed for the ULT and among the surface treatments, the use of SBU enabled greater BS, however it did not influence the nanoleakage at the cement-resin interface. It is suggested that semi-direct composite resin restorations can be cemented with ULT with SBU as a resin surface treatment, as well as with U200, without the need for any chemical treatment in the restoration (AU).

Conservative Substitution of Fractured Ceramic Onlays Using Self-Adhesive Cement: Case Report / Substituição Conservadora de Onlays Cerâmicas Fraturadas Utilizando Cimento Autoadesivo: Relato de Caso

The advances in bonding of ceramics and self-adhesive resin cements to tooth structure make this treatment a feasible alternative to restore posterior teeth. This case report described the removal of two fractured onlays and the fabrication of new lithium disilicate onlays cemented with self-adhesive resin cement. The rationale for various choices in this treatment protocol is detailed with reference to the pertinent literature. It is concluded that the clinical success of the technique depends on the correct identification of the case for which this treatment is appropriate and on the successful execution of the clinical steps involved. (AU)

Os avanços na adesão de cerâmicas e cimentos resinosos autoadesivos à estrutura dentária tornam este tratamento uma alternativa viável para restaurar os dentes posteriores. Ester relato de caso descreveu a remoção de duas onlays fraturadas e confecção de novas onlays de dissilicato de lítio cimentadas com cimento resinoso auto-adesivo. A justificativa para várias escolhas neste protocolo de tratamento é detalhada com referência à literatura pertinente. O sucesso clínico da técnica depende da correta identificação do caso para o qual este tratamento é adequado e da execução bem-sucedida das etapas clínicas envolvidas. (AU)

Restaurações cerâmicas delgadas sobre dentes sem preparo em diferentes regiões dos arcos dentais: relato de 2 casos clínicos / Thin ceramic restorations on unprepared teeth in different regions of the dental arches: report of 2 clinical cases / Restauraciones cerámicas finas en dientes no preparados en diferentes regiones de los arcos dentales: reporte de 2 casos clínicos

As reforçadas propriedades intrínsecas dos materiais cerâmicos, associados à adesão resinosa fundamentam a desenvoltura de técnicas restauradoras mais simplificadas, conservadoras e sem a necessidade de preparo dental prévio seja em dentição anterior ou posterior. Assim sendo, o trabalho tem como objetivo apresentar dois casos clínicos os quais abordaram a confecção de restaurações delgadas em dissilicato de lítio cimentadas sobre diferentes áreas dos arcos dentários, enfatizando o mesmo protocolo clínico, ou seja, ausência de preparos dentais e consequentemente a cimentação resinosa adesiva das restaurações. Caso Clínico 1: laminados cerâmicos nos elementos 13, 12, 11, 21, 22 e 23; Caso Clínico 2: facetas delgadas sobre os elementos 34, 35, 36 e 37. Ambos os casos clínicos com 1 ano de acompanhamento após a cimentação das restaurações. Conclui-se que houve a recuperação da estética e da função em ambos os casos apresentados e a confiabilidade e o sucesso em longo prazo do protocolo clínico descrito estão diretamente relacionados ao substrato dentário, aos fatores de adesividade dos materiais e as propriedades intrínsecas das cerâmicas(AU)

The reinforced intrinsic properties of the ceramic materials, associated with the resinous adhesion, support the development of restorative techniques that are simplified, conservative and without the need of previous dental preparation, either in anterior or posterior dentition. The objective of this study was to present two clinical cases which used thin restorations in lithium disilicate cemented in different areas of the dental arches, emphasizing the same clinical protocol, that is, the absence of dental preparations and, consequently, resinous cementation. Clinical Case 1: ceramic laminates veneers in elements 13, 12, 11, 21, 22 and 23; Clinical case 2: thin ceramic restorations on elements 34, 35, 36 and 37. At both cases with 1 year of follow-up after cementation of the restorations. It was concluded that there was recovery of aesthetics and function in both cases presented and the reliability and long-term success of the described clinical protocol are directly related to the dental substrate, the material adhesion factors and the intrinsic properties of the ceramics(AU)

Las propiedades intrínsecas reforzadas de los materiales cerámicos, asociadas con la adhesión resinosa, apoyan el desarrollo de técnicas restaurativas que son simplificadas, conservadoras y sin la necesidad de una preparación dental previa, ya sea en la dentición anterior o posterior. El objetivo de este estudio fue presentar dos casos clínicos que utilizaron restauraciones delgadas en disilicato de litio cementadas en diferentes áreas de los arcos dentales, enfatizando el mismo protocolo clínico, es decir, la ausencia de preparaciones dentales y, en consecuencia, la cementación resinosa. Caso Clínico 1: carillas cerámicas en los elementos 13, 12, 11, 21, 22 y 23; Caso clínico 2: restauraciones cerámicas delgadas en los elementos 34, 35, 36 y 37. Ambos casos con 1 año de seguimiento después de la cementación de las restauraciones. Se concluyó que hubo recuperación de la estética y la función en ambos casos presentados y la fiabilidad y el éxito a largo plazo del protocolo clínico descrito están directamente relacionados con el sustrato dental, los factores de adhesión del material y las propiedades intrínsecas de la cerámica(AU)

Efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina / The effect of age on morphological, chemical and physical aspects of human and bovine root dentin

Dentes bovinos têm sido utilizados como substitutos aos humanos em pesquisas odontológicas. Entretanto, faltam dados que suportem o uso da dentina radicular bovina, sobretudo, que analisem o efeito da idade nas propriedades do substrato. Assim, analisou-se o efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina, em função dos terços da raiz. Trata-se de um estudo experimental, in vitro, aprovado pelo Comitê de Ética em Pesquisa (COEP-UFMG 1.803.933) e pela Comissão de Ética no Uso de Animais (CEUAUFMG 372/2016). A amostra foi composta por dentes unirradiculares, cujas dentinas radiculares foram categorizadas em: humana jovem (HJ, 20-30 anos); humana madura (HM, acima de 60 anos); bovina jovem (BJ, 24-36 meses); e bovina adulta (BA, acima de 48 meses). Os dentes foram seccionados abaixo da junção amelocementária e ao longo eixo da raiz, para a obtenção de hemisecções. Uma hemisecção foi escolhida e cortes foram feitos para a obtenção dos espécimes, conforme cada método de análise. Para as análises dos aspectos morfológicos ­ número, diâmetro e área dos túbulos dentinários ­ os espécimes foram analisados em Microscópio Eletrônico de Varredura. A composição química foi analisada por Espectroscopia de Raios X por Dispersão em Energia, Espectroscopia por Comprimento de Onda Dispersivo e Espectroscopia Raman por Transformada de Fourier. Na análise das propriedades mecânicas, os espécimes foram submetidos aos testes de nanoindentação, resistência à flexão em três pontos e compressão. Para a análise da resistência ao cisalhamento por extrusão, as raízes receberam tratamento endodôntico e foram fixados pinos de fibra de vidro com cimentos resinosos (dual convencional e autoadesivo). As raízes foram seccionadas nos terços radiculares e os espécimes testados em máquina universal de ensaios. Adicionalmente, avaliou-se o grau de conversão dos cimentos resinosos. Os dados foram analisados em software estatístico, nível de significância de 5%. A HM apresentou os menores valores para número, diâmetro e área de túbulos dentinários (p<0,05). A HM apresentou maiores valores de cálcio, razão Ca/P e concentração mineral relativa, com diminuição na organização e qualidade do colágeno (p<0,05). A HM apresentou os maiores valores de nanodureza, módulo de elasticidade e resistência à compressão, mas os menores valores de resistência à flexão e módulo de elasticidade à flexão (p<0,05). A HM apresentou os menores valores de resistência de união, com diferenças entre os terços radiculares (p<0,05). O grau de conversão dos cimentos apresentou uma diminuição ao longo dos terços radiculares (p<0,05). Concluiu-se que a idade possui um efeito nos aspectos morfológicos, químicos e físicos da dentina radicular humana, sem efeito na dentina bovina. Assim, quando da necessidade de substituição da dentina radicular humana pela bovina em pesquisas, é necessário considerar o efeito da idade nos desfechos analisados.

Bovine teeth have been used as a substitute for human teeth in dental research. However, there is a lack of data that support the use of bovine root dentin, mainly, that analyze the effect of age on the properties of the substrate. Thus, the effect of age on the morphological, chemical and physical aspects of human and bovine root dentin was analyzed, in function of the root thirds. This is an in vitro experimental study, approved by the Research Ethics Committee (protocol number: 1.803.933) and the Ethics Committee on the Use of Animals (protocol number: 372/2016). The sample was composed of single-rooted teeth and root dentin was categorized into: young human (YH, 20-30 years); old human (OH, above 60 years); young bovine (YB, 24-36 months); and adult bovine (AB, over 48 months). The roots were sectioned below the cement-enamel and longitudinally to produce two hemi-sections. One hemi-section was chosen and sections were made to obtain the specimens, according to each method of analysis. For the analyzes of the morphological aspects - number, diameter and area of the dentinal tubules - the specimens were analyzed in Scanning Electron Microscope. The chemical composition was analysed by Energy Dispersive Spectroscopy, Wavelength Dispersive Spectroscopy and Fourier Transformed Raman Spectroscopy. In the analysis of the mechanical properties, the specimens were submitted to nano-indentation, three-point flexural and compression tests. For the analysis of the push-out bond strength test, the roots received endodontic treatment and fiber post with resin cements (conventional and selfadhesive dual) were fixed. The roots were sectioned in the root thirds and the specimens tested in a universal testing machine. Additionally, the degree of conversion of the resin cements was evaluated. The data were analyzed in statistical software, level of significance of 5%. The OH presented the lowest values for number, diameter and area of dentinal tubules (p<0.05). OH showed higher values of calcium, Ca/P ratio and relative mineral concentration, with decrease in the organization and quality of the collagen (p<0.05). The OH showed the highest values of nano-hardness, elastic modulus and compressive strength, but the lowest values of flexural strength and flexural modulus (p<0.05). The OH presented the lowest values of bond strength, with differences among the root thirds (p<0.05). The degree of conversion of the cements showed a decrease along the root thirds (p<0.05). It was concluded that age has an effect on the morphological, chemical and physical aspects of human root dentin, with no effect on bovine dentin. Thus, when it is necessary to replace the human root dentin by the bovine in research, it is necessary to consider the effect of age on the analysed outcomes.

Efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina / The effect of age on morphological, chemical and physical aspects of human and bovine root dentin

Dentes bovinos têm sido utilizados como substitutos aos humanos em pesquisas odontológicas. Entretanto, faltam dados que suportem o uso da dentina radicular bovina, sobretudo, que analisem o efeito da idade nas propriedades do substrato. Assim, analisou-se o efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina, em função dos terços da raiz. Trata-se de um estudo experimental, in vitro, aprovado pelo Comitê de Ética em Pesquisa (COEP-UFMG 1.803.933) e pela Comissão de Ética no Uso de Animais (CEUAUFMG 372/2016). A amostra foi composta por dentes unirradiculares, cujas dentinas radiculares foram categorizadas em: humana jovem (HJ, 20-30 anos); humana madura (HM, acima de 60 anos); bovina jovem (BJ, 24-36 meses); e bovina adulta (BA, acima de 48 meses). Os dentes foram seccionados abaixo da junção amelocementária e ao longo eixo da raiz, para a obtenção de hemisecções. Uma hemisecção foi escolhida e cortes foram feitos para a obtenção dos espécimes, conforme cada método de análise. Para as análises dos aspectos morfológicos ­ número, diâmetro e área dos túbulos dentinários ­ os espécimes foram analisados em Microscópio Eletrônico de Varredura. A composição química foi analisada por Espectroscopia de Raios X por Dispersão em Energia, Espectroscopia por Comprimento de Onda Dispersivo e Espectroscopia Raman por Transformada de Fourier. Na análise das propriedades mecânicas, os espécimes foram submetidos aos testes de nanoindentação, resistência à flexão em três pontos e compressão. Para a análise da resistência ao cisalhamento por extrusão, as raízes receberam tratamento endodôntico e foram fixados pinos de fibra de vidro com cimentos resinosos (dual convencional e autoadesivo). As raízes foram seccionadas nos terços radiculares e os espécimes testados em máquina universal de ensaios. Adicionalmente, avaliou-se o grau de conversão dos cimentos resinosos. Os dados foram analisados em software estatístico, nível de significância de 5%. A HM apresentou os menores valores para número, diâmetro e área de túbulos dentinários (p<0,05). A HM apresentou maiores valores de cálcio, razão Ca/P e concentração mineral relativa, com diminuição na organização e qualidade do colágeno (p<0,05). A HM apresentou os maiores valores de nanodureza, módulo de elasticidade e resistência à compressão, mas os menores valores de resistência à flexão e módulo de elasticidade à flexão (p<0,05). A HM apresentou os menores valores de resistência de união, com diferenças entre os terços radiculares (p<0,05). O grau de conversão dos cimentos apresentou uma diminuição ao longo dos terços radiculares (p<0,05). Concluiu-se que a idade possui um efeito nos aspectos morfológicos, químicos e físicos da dentina radicular humana, sem efeito na dentina bovina. Assim, quando da necessidade de substituição da dentina radicular humana pela bovina em pesquisas, é necessário considerar o efeito da idade nos desfechos analisados.

Bovine teeth have been used as a substitute for human teeth in dental research. However, there is a lack of data that support the use of bovine root dentin, mainly, that analyze the effect of age on the properties of the substrate. Thus, the effect of age on the morphological, chemical and physical aspects of human and bovine root dentin was analyzed, in function of the root thirds. This is an in vitro experimental study, approved by the Research Ethics Committee (protocol number: 1.803.933) and the Ethics Committee on the Use of Animals (protocol number: 372/2016). The sample was composed of single-rooted teeth and root dentin was categorized into: young human (YH, 20-30 years); old human (OH, above 60 years); young bovine (YB, 24-36 months); and adult bovine (AB, over 48 months). The roots were sectioned below the cement-enamel and longitudinally to produce two hemi-sections. One hemi-section was chosen and sections were made to obtain the specimens, according to each method of analysis. For the analyzes of the morphological aspects - number, diameter and area of the dentinal tubules - the specimens were analyzed in Scanning Electron Microscope. The chemical composition was analysed by Energy Dispersive Spectroscopy, Wavelength Dispersive Spectroscopy and Fourier Transformed Raman Spectroscopy. In the analysis of the mechanical properties, the specimens were submitted to nano-indentation, three-point flexural and compression tests. For the analysis of the push-out bond strength test, the roots received endodontic treatment and fiber post with resin cements (conventional and selfadhesive dual) were fixed. The roots were sectioned in the root thirds and the specimens tested in a universal testing machine. Additionally, the degree of conversion of the resin cements was evaluated. The data were analyzed in statistical software, level of significance of 5%. The OH presented the lowest values for number, diameter and area of dentinal tubules (p<0.05). OH showed higher values of calcium, Ca/P ratio and relative mineral concentration, with decrease in the organization and quality of the collagen (p<0.05). The OH showed the highest values of nano-hardness, elastic modulus and compressive strength, but the lowest values of flexural strength and flexural modulus (p<0.05). The OH presented the lowest values of bond strength, with differences among the root thirds (p<0.05). The degree of conversion of the cements showed a decrease along the root thirds (p<0.05). It was concluded that age has an effect on the morphological, chemical and physical aspects of human root dentin, with no effect on bovine dentin. Thus, when it is necessary to replace the human root dentin by the bovine in research, it is necessary to consider the effect of age on the analysed outcomes.

Influência de diferentes tipos de retentores intrarradiculares na resistência de união de um cimento resinoso autoadesivo à dentina radicular bovina / Influência de diferentes tipos de retentores intrarradiculares de fibra de vidro na resistência de união de um cimento resinoso autoadesivo à dentina radicular bovina / Influence of different types of fiberglass intraradicular retainers on the bond strength of a self-adhesive resin cement to bovine root dentin

Este estudo experimental in vitro seguindo o delineamento de blocos aleatorizados avaliou a resistência de união de diferentes tipos de retentores intrarradiculares de fibra de vidro à dentina radicular bovina, em dentes tratados endodonticamente e extensamente destruídos. Os incisivos inferiores bovinos obtidos foram limpos manualmente. Aqueles que preencheram os critérios de inclusão foram seccionados na junção cemento-esmalte. Em seguida, o comprimento e o diâmetro das raízes foram padronizados e elas foram tratadas endodonticamente e preparadas com brocas do tipo Largo números 2, 3 e 4. Após a utilização da sequência de brocas Largo, foi utilizada a broca número 3, constituinte do conjunto de pinos de fibra de vidro EXACTO. O comprimento de trabalho adotado foi de 11 mm, e foi deixado remanescente de material obturador de 4 mm. A ponta adiamantada número 4137 (ø = 2,5 mm) foi utilizada nos 3,5 mm mais coronários das raízes para simular casos de grande perda de substrato dentário. As raízes preparadas (n=33) foram divididas aleatoriamente em 3 grupos de acordo com o tipo de pino utilizado: 1) pino de fibra de vidro convencional; 2) pino de fibra de vidro reembasado com resina composta; 3) pino de fibra de vidro fresado no sistema CAD/CAM. Após a cimentação dos pinos com o mesmo cimento resinoso autoadesivo (RelyXÔ U200, 3M ESPE), cada raiz foi seccionada. Obtiveram-se 6 espécimes de cada raiz, os quais foram submetidos ao teste de cisalhamento por extrusão (push-out). Um corpo de prova representativo de cada grupo experimental (n=3) foi submetido à análise em Microscopia Eletrônica de Varredura (MEV), para que fossem avaliadas a adaptação marginal à dentina, a espessura e presença de bolhas na película do cimento resinoso de cada grupo nos terços coronal, médio e apical das raízes. O nível de significância para análise estatística foi de 5% e o poder do teste de 80%. Os valores de resistência de união e os terços radiculares foram comparados utilizando-se One-way ANOVA e teste de Tukey, exceto para o grupo de pinos reembasados, que foram comparados pelos testes Kruskal-Wallis e Games-Howell. O grupo de pinos reembasados obteve melhor desempenho que os outros grupos no terço coronal (8,92 MPa) (p=0,010) e foi o único grupo em que a resistência de união foi afetada pelo terço radicular, sendo o apical aquele com pior desempenho (4,51 MPa) (p=0,037). A fratura predominante nos diferentes grupos de retentores intrarradiculares foi do tipo adesiva entre o cimento e a dentina, exceto nos terços coronais dos grupos reembasado e fresado, onde a fratura principal foi do tipo coesiva em dentina. Concluiu-se que o tipo de retentor intrarradicular e o nível de acesso ao conduto radicular afetaram a resistência de união.

This study evaluated the bond strength of different fiberglass post types to root dentin in cases of severely damaged endodontically treated teeth. A pilot study was carried out and sample size was calculated from the results. Around 340 bovine teeth were obtained in a certified slaughterhouse. Teeth were cleaned and sectioned at dentinenamel's junction. After selection criteria were met, teeth were selected, the roots were endodontically treated and root canals were prepared with Largo burs #2, 3 and 4. After the treatment with Largo bur #4, the specific bur from EXACTO fiberglass post kit was used. The working length was 11 mm and 4 mm gutta-percha remnant were left to seal the apical region. The #4137 diamond bur (ø 2,5 mm) was used on the roots' most coronal 3,5 mm region to simulate extensive loss of tooth structure. The prepared roots (n=33) received different types of fiberglass posts, which were fixed with self-adhesive resin cement (RelyXÔ U200, 3M ESPE), and were randomly divided into 3 groups: 1) conventional glass fiber posts; 2) relined glass fiber posts; 3) glass fiber posts milled on CAD/CAM units. After posts fixing procedure, each root (n=30) was sectioned in different root thirds (coronal, medium and apical), originating 2 specimens/third in a total 6 specimens/root, that were submitted to push-out bond strength test. Other additional root from each experimental group (n=3) was prepared and analyzed using Scanning Electron Microscopy to describe the marginal adaptation to radicular dentin, presence of voids and thickness of the resin cement film, in each root third (coronal, medial and apical. To perform statistical analysis, alpha was preset at 0.05 and 80% power test. The values of bond strength and root third was analyzed using One-way ANOVA and Tukey post-hoc test. The relined fiberglass post group presented better performance than the other two groups at the coronal level (8,92 MPa) (p=0,010). Additionally, the relined fiber post group was also the only group which bond strength values were influenced by root third, and the apical third reported the worst results (4,51MPa) (p=0,037). Therefore, it was concluded that the type of fiberglass post and the root third affected the bond strength to root dentin.

Avaliação da resistência de união dos cimentos resinosos aplicados sobre a cerâmica feldspática / Evaluation of the resistance of resin cements on a feldspathic ceramic

Cimentação é uma etapa extremamente importante para o sucesso de reabilitações estéticas utilizando cerâmicas, tornando-se fundamental o entendimento dos materiais utilizados nesse processo, como os cimentos e agentes de união. Avaliou-se a resistência de união gerada por diferentes tratamentos de superfície em cerâmica feldspática com cimentos resinosos utilizando diferentes agentes de união. Foram confeccionados 24 discos de cerâmica feldspática (Super porcelain EX-3, Noritake) e divididos de acordo com o agente de união utilizado: Grupo SAU - sem aplicação de agentes; Grupo SIL - aplicado silano (RelyX cerâmic Primer, 3M ESPE); Grupo ADU - aplicado adesivo universal (Single Bond Universal, 3M ESPE) e Grupo SIL+ADU - aplicado silano e adesivo universal. Sobre cada amostra foram confeccionados 4 cilindros de cimentos resinosos: RelyX ARC (RXA) (3M ESPE) e RelyX Ultimate (RXU) (3M ESPE), totalizando 12 tubos de cada cimento por grupo. Então, foram submetidos ao teste de microcisalhamento em máquina de ensaios universais Série 23 EMIC (Instron Brasil) e verificado em microscópio o padrão de fratura gerado. A comparação entre grupos usando cimento RXA mostrou que, utilizando silano combinado ou não ao adesivo, proporcionou melhores resultados que os demais grupos (p=0,05). Utilizando o mesmo tratamento de superfície, não foi verificada diferença significante entre os cimentos, exceto para Grupo SAU (p=0,05). Concluiu-se que utilizar silano combinado ou não a adesivos universais melhora a adesão de alguns cimentos utilizados na cimentação de cerâmicas feldspáticas. Quando aplicado o mesmo agente, não há diferença entre os cimentos testados (AU).

Cementation is an extremely important step for the success of aesthetic restorations using ceramics, making it fundamental to understand the materials used in this process, such as cements and bonding agents. This study aimed to evaluate the bond strength generated by different surface treatments in feldspathic ceramic with resin cements using different bonding agents. Twenty-four feldspathic ceramic discs (Super porcelain EX-3, Noritake) were prepared and divided according to the bonding agent used: Group SAU - without application; Group SIL - applied silane (RelyX ceramics Primer, 3M ESPE); Group ADU - applied universal adhesive (Universal Bond Single, 3M ESPE); and Group SIL+ADU - silane and universal adhesive. For each sample, 4 cylinders of resin cements were made: RelyX ARC (RXA) (3M ESPE) and RelyX Ultimate (RXU) (3M ESPE), totaling 12 tubes of each cement per group. Then, they were submitted to the micro-shear test in the universal Series 23 EMIC assay (Instron Brasil) and microscopically verified the generated fracture pattern. The comparison between groups using RXA cement showed that using silane combined or not with the adhesive gave better results than the other groups (p=0,05). Using the same surface treatment, no significant difference was observed between the cements, except for Group SAU (p<0.05). It was concluded that using silane combined or not with universal adhesives improves the adhesion of some cements used in the cementation of feldspathic ceramics. When applied the same agent, there is no difference between the cements tested (AU).

Evaluation of the effect of chlorhexidine and sodium hypochlorite in adhesive cementation of fiber posts - in vitro study / Avaliação do efeito da clorexidina e do hipoclorito de sódio na cimentação adesiva de pinos - estudo in vitro

Abstract Introduction The attachment of fiberglass posts is achieved through an adhesive process. Failures in adhesion may occur due to the hydrolytic degradation of the adhesives, or to the degradation of the collagen fibres of the hybrid layer by intrinsic enzymes. Objective To evaluate the effect of chlorhexidine and sodium hypochlorite treatment on bond strength to dentin. Material and method Thirty bovine roots were randomly distributed into 3 groups (n=10): a) Control, b) 2% Chlorhexidine, and c) 5% Sodium Hypochlorite. Next, RelyX® ARC resin cement was used to cement the post. Each specimen resulted in samples from the three root thirds that were submitted to the pushout test (MPa) at 24 hours and 12 months. Bond strength values were analysed using the Kolmogorov-Smirnov, 3-way ANOVA and Tukey tests. The fracture mode of the pin was also analysed using stereomicroscopy. Result There were no significant differences between treatments at the immediate time (p=0.0644) or in the interaction of factors (p=0.1935). After one year, the experimental groups showed no significant differences in bond strength in relation to the control group, with the exception of the cervical third of the chlorohexidine group in which there was a significant loss of adhesion. As for the fracture mode, there was a predominance of the mixed type in all groups and thirds. Conclusion The use of chlorhexidine or hypochlorite provides neither benefits nor losses in the adhesive bond strength of fiberglass posts. However, there is an influence of the root thirds, with the worst bond strength in the apical third.

Resumo Introdução A fixação de pinos de fibra de vidro é realizada através de um processo adesivo. Falhas podem ocorrer na adesão devido à degradação hidrolítica dos adesivos, ou pela degradação das fibras colágenas da camada híbrida por enzimas intrínsecas. Objetivo Avaliar o efeito do tratamento com clorexidina e hipoclorito de sódio sobre a resistência de união adesiva à dentina. Material e método Trinta raízes bovinas foram distribuídas aleatoriamente em 3 grupos (n=10): a) Controle, b) Clorexidina 2% e c) Hipoclorito de Sódio 5%. Após, para a cimentação do pino radicular, utilizou-se o cimento resinoso RelyX® ARC. Cada espécime resultou corpos-de-prova dos três terços radiculares, os quais foram submetidos ao teste de pushout (MPa) nos períodos de 24 horas e 12 meses. Valores de resistência de união foram analisados pelos testes de Kolmogorov-Smirnov, ANOVA (three-way) e de Tukey. Analisou-se ainda o modo de fratura do pino, através de estereomicroscopia. Resultado Não houve diferenças significativas entre tratamento no tempo imediato (p=0,0644) ou na interação dos fatores (p=0,1935). Após um ano, os grupos experimentais não promoveram diferença significante na resistência de união em relação ao controle, com exceção do terço cervical do grupo clorexidina, onde houve uma perda significativa de adesão. Quanto ao modo de fratura, houve predominância do tipo mista em todos os grupos e terços. Conclusão O uso de clorexidina ou hipoclorito não promove benefícios ou prejuízos na resistência de união adesiva de pinos de fibra, mas há influência dos terços radiculares, sendo a pior resistência de união no terço apical.